铬渣作水泥矿化剂的技术条件研究

Research on Technical Conditions of Chromium-Containing Residue as Cement Mineralizer

摘要: 通过生产性试验,提出了铬渣作水泥矿化剂的最佳工艺技术条件为:立窑法水泥生产,投加量为2%,炉温控制在1 300~1 400℃。按此工艺条件可以使水泥强度提高6%~10%,并使Cr6+还原率达96.2%。
- 水泥 /
- 环境效应 /
- 铬渣 /
- 矿化剂 /
- 工艺条件
Abstract: The best technical conditions of chromium-containing residue acting as cement mineralizer are obtained in pilot production. The proper additive ratio of chromium-containing residue in producing cement in a vertical furnace is 2%; and the temperature should be controlled at 1 300℃to 1 400℃. With this technique, the cement strength is improved by 6% to 10%, and the reduction ratio of Cr6+is 96.2%.
- cements /
- environmental effect /
- chromium dregs /
- mineralizer /
- technical condition