Influences of Laser Treatment on Properties of Ni-P Layers Plated on Aluminum Substrates
-
摘要: 用Nd-YAG脉冲激光处理铝合金基体上化学镀的Ni-P合金镀层.与未处理的合金镀层相比,当激光能量密度为0.515 GW/m2时,Ni-P合金镀层的性能有明显提高,表面粗糙度降低而与基体的界面结合力增大,耐腐蚀性能也有显著的提高.
-
关键词:
- Nd-YAG脉冲激光 /
- 化学镀 /
- Ni-P镀层 /
- 表面改性
Abstract: A Nd-YAG pulsed laser was used to modify electroless plated Ni-P layers on aluminum substrates.The Ni-P layers were successfully modified with a laser power density of 0.515 GW/m2.The modified Ni-P layers exhibit smoother surface,better bonding strength with the substrate,and better corrosion resistance compared with untreated layers.-
Key words:
- Nd-YAG pulsed laser /
- electroless plating /
- Ni-P layer /
- surface modification
-
ASHASSI-SORKHABI H,RAFIZADEH S H.Effect of coating time and heat treatment on structures and corrosion characteristics of electroless Ni-P alloy deposits[J].Surf.and Coat.Technol.,2004,176 (3):318-326.[2] 李宁,袁国伟,黎德育.化学镀镍基合金理论与技术[M].哈尔滨:哈尔滨工业大学出版社,2000:69-72.[3] 沃尔夫冈·里德尔.化学镀镍[M].罗守福译.上海:上海交通大学出版社,1996:48.[4] SONG J Y,JIN Y.Residual stress measurements in electroless plated Ni-P films[J].Thin Solid Films,2002,415 (1):167-172.[5] GU C D,LIAN J S.High corrosion-resistant Ni-P/Ni/Ni-P multilayer coatings on steel[J].Surf.and Coat.Technol.,2005,197(1):61-67.[6] YU J J,LU Y F.Laser-induced ripple structures on Ni-P substrates[J].Appl.Surf.Sci.,1999,148(3):248-252.[7] GARCIA-ALONSO M C,ESCUDERO M L.The corrosion behavinur of laser treated Ni-P alloy coatings on mild steel[J].Cones.SOi.,1996,38(3):515-530.[8] de DAMBORENEA J.Surface modification of metals by high power lasers[J].Surf.and Coat.Technol.,1998,100-101(1-3):377-382.[9] ARRANZ A,PALACIO C.Study of Ni-A1 interface formation[J].Thin Solid Films,1998,317(1):55-58.[10] 武汉材料保护研究所.GB 5270-85金属基体上的金属覆盖层(电沉积和化学沉积层)附着强度试验方法[S].北京:机械工业出版社,1985. -
点击查看大图
计量
- 文章访问数: 1335
- HTML全文浏览量: 73
- PDF下载量: 489
- 被引次数: 0
下载: